QUALITY SUBSTRATE MATERIAL
Our electrodes are manufactured from high-tensile titanium, which meets commercially Grade I/II standards.
|
Element |
Grade I |
Grade II |
|
Iron (Fe) |
0.20% max. |
0.30% max. |
|
Carbon (C) |
0.08% max. |
0.08% max. |
|
Nitrogen (N) |
0.03% max. |
0.03% max. |
|
Hydrogen (H) |
0.015% max. |
0.015% max. |
|
Oxygen (O) |
0.18% max. |
0.25% max. |
|
Titanium (Ti) |
Remainder |
Remainder |
LONG SERVICE COATING
Using state-of-the-art technology, the titanium base is taken to a high temperature ( ≥1200 °C) in a vacuum sintering furnace ensuring total adhesion of the coating. Thus, the coating consumption rate is extremely low and uniform, measured in milligrams per ampere-year.
|
Technical Measurement |
Performance |
|
Coating Composition |
Platinum |
|
Coating Thickness |
0.5~5 μm |
WORKING ENVIRONMENT
|
Technical Measurement |
Performance |
|
Current Density |
≤ 5000 A/m² |
|
Operating Voltage |
≤ 24V |
|
pH Range |
1~12 |
|
Temperature |
< 80 °C |
|
Fluoride Ion Content |
< 50 mg/L |