QUALITY SUBSTRATE MATERIAL
Our electrodes are manufactured from high-tensile titanium, which meets commercially Grade I/II standards.
Element |
Grade I |
Grade II |
Iron (Fe) |
0.20% max. |
0.30% max. |
Carbon (C) |
0.08% max. |
0.08% max. |
Nitrogen (N) |
0.03% max. |
0.03% max. |
Hydrogen (H) |
0.015% max. |
0.015% max. |
Oxygen (O) |
0.18% max. |
0.25% max. |
Titanium (Ti) |
Remainder |
Remainder |
LONG SERVICE COATING
Using state-of-the-art technology, the titanium base is taken to a high temperature ( ≥1200 °C) in a vacuum sintering furnace ensuring total adhesion of the coating. Thus, the coating consumption rate is extremely low and uniform, measured in milligrams per ampere-year.
Technical Measurement |
Performance |
Coating Composition |
Iridium Oxides (IrO2), Tantalum Oxides (Ta2O5) |
Coating Thickness |
6~12 μm |
WORKING ENVIRONMENT
Technical Measurement |
Performance |
Current Density |
500~800 A/m² |
Operating Voltage |
≤ 24V |
pH Range |
1~14 |
Temperature |
< 85 °C |
Fluoride Ion Content |
< 50 mg/L |