QUALITY SUBSTRATE MATERIAL
Our electrodes are manufactured from high-purity niobium, which meets ASTM 391 standards.
|
Element |
Reactor Grade (R04200) |
Commercial Grade (R04210) |
|
Tantalum (Ta) |
0.1% |
0.3% |
|
Tungsten (W) |
0.03% | 0.05% |
|
Titanium (Ti) |
0.02% |
0.03% |
|
Oxygen (O) |
0.015% |
0.025% |
|
Molybdenum (Mo) |
0.01% |
0.02% |
|
Carbon (C) |
0.01% |
0.01% |
|
Nitrogen (N) |
0.01% |
0.01% |
|
Iron (Fe) |
0.005% |
0.01% |
|
Silicon (Si) |
0.004% |
0.01% |
| Nickel (Ni) |
0.002% |
0.005% |
|
Hydrogen (H) |
0.0015% |
0.0015% |
|
Niobium (Nb) |
Remainder |
Remainder |
LONG SERVICE COATING
Using state-of-the-art technology, the titanium base is taken to a high temperature ( ≥1200 °C) in a vacuum sintering furnace ensuring total adhesion of the coating. Thus, the coating consumption rate is extremely low and uniform, measured in milligrams per ampere-year.
|
Technical Measurement |
Performance |
|
Coating Composition |
Platinum |
|
Coating Thickness |
0.5~5 μm |
WORKING ENVIRONMENT
|
Technical Measurement |
Performance |
|
Current Density |
500~800 A/m² |
|
Operating Voltage |
1~2 V |
|
pH Range |
1~14 |
|
Temperature |
< 85 °C |
|
Fluoride Ion Content |
< 50 mg/L |